Plastic Film-Laminated Steel Sheets

Polyester-based plastic film-laminated steel sheets
EXUMTM

EXUM incorporates galvanized steel sheets, stainless steel sheets, and aluminum alloy sheets as a base material. EXUM is a polyester-based plastic film-laminated steel sheet manufactured by our multi-layer extrusion technology.
This material is primarily used in interior applications due to the combination of metal strength, workability, and design qualities.

Characteristics

  • EXUM has a surface hardness higher than PVC film and polyolefin film.
    Many options are available including solid colors, printed patterns, high-gloss options to satisfy various design requirements.
  • This material has excellent bending properties.
  • EXUM can have a vivid appearance with the mirror finish.
  • Emboss
  • High-Gloss

Applications

EXUM is utilized in various interior applications due to its beautiful appearance and excellent workability.

  • interior applications
    : Unit baths, elevators, etc.
  • Low-current devices
    : Refrigerators, etc.
  • Other
  • Unit bathsUnit baths
  • ElevatorsElevators

Manufacturing Scope and Order Conditions

  • Lot
    A lot of 2.5 tons or more is required to order a product having the same specifications such as the same sheet thickness, width, color and embossing.

    * Please order in lots of at least 2.5 tons as special request lots smaller than this will require an extra fee.

Performance

* Table can be scrolled horizontally

Specific test Test conditions Criteria EXUM
Adhesion Conformal Erichsen
6 mm extrusion
25±5°C No separation Nothing abnormal
Bendability Adhesion and bending test 25±5°C, 0T No cracking, breakage, and separation Nothing abnormal
Processability at low temperature 90° bend test 0±1°C, R=2 No cracking, breakage, and separation Nothing abnormal
Resistance to boiling water Dipping in boiling water Submerged in water for 5 minutes after 60 minutes of immersion No shrinkage, cracking, breakage, creasing, separation, and marked fading Nothing abnormal
Chemical resistance 5-minute immersion
(20±2°C)
10% hydrochloric acid No rust, stain, and marked fading Nothing abnormal
Saturated calcium hydroxide
10% sulfuric acid
Aqueous solution of sodium hydroxide (100 g/L)
Ethanol
Kerosene
Corrosion resistance Complies with salt spray test
JIS Z 2371
JIS K 6744
Type C: 1,000 hours
No rust Nothing abnormal
Self-extinguishability Gas burner heating for 20 seconds Extinguishes immediately Extinguishes immediately within 10 seconds

*1 The data described above represents the specified values in our company and does not represent guaranteed values.

*2 Please contact us to inquire on the certification of fire-resistant materials.